Technology
SLS
Maximal size for series production
650 x 320 x 560 mm
Maximal size for prototyping
350 x 320 x 560 mm
Heat distortion temperature (at 0.45MPa)
175°C
Tensile strength at break
48 MPa
Elongation at break
20 %
Flexural modulus
1500 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²
Datasheet
Technology
SLS
Maximal size for series production
630 x 330 x 550 mm
Maximal size for prototyping
630 x 330 x 550 mm
Heat distortion temperature (at 0.45MPa)
179°C
Tensile strength at break
51 MPa
Elongation at break
9 %
Flexural modulus
2900 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²
Datasheet
Technology
SLS
Maximal size for series production
630 x 330 x 550 mm
Maximal size for prototyping
630 x 330 x 550 mm
Heat distortion temperature (at 0.45MPa)
179°C
Tensile strength at break
51 MPa
Elongation at break
4 %
Flexural modulus
3600 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²
Datasheet
Technology
MJF
Maximal size for series production
256 x 340 x 360 mm
Maximal size for prototyping
256 x 340 x 360 mm
Heat distortion temperature (at 0.45MPa)
175°C
Tensile strength at break
48 MPa
Elongation at break
20 %
Flexural modulus
1730 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²
Datasheet
Technology
MJF
Maximal size for series production
256 x 340 x 360 mm
Maximal size for prototyping
256 x 340 x 360 mm
Heat distortion temperature (at 0.45MPa)
175°C
Tensile strength at break
48 MPa
Elongation at break
20 %
Flexural modulus
1730 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²
Datasheet
Technology
SLS
Maximal size for series production
480 x 480 x 430 mm
Maximal size for prototyping
480 x 480 x 430 mm
Heat distortion temperature (at 0.45MPa)
100°C
Tensile strength at break
21 MPa
Elongation at break
500 %
Flexural modulus
700 MPa
Izod impact strength (at 23°C, notched)
---
Datasheet
Technology
SLS
Maximal size for series production
110 x 150 x 245 mm
Maximal size for prototyping
110 x 150 x 245 mm
Heat distortion temperatur (at 0.45MPa)
---
Tensile strengthe at break
3,7 MPa
Elongation at break
136 %
Flexural modulus
---
Izod impact strength (at 23°C, notched)
---
Datasheet
Technology
DMLS
Maximal size for series production
250 x 250 x 280 mm
Maximal size for prototyping
250 x 250 x 280 mm
Heat distortion temperature (at 0.45MPa)
---
Tensile strength at break
530 MPa
Elongation at break
50 %
Flexural modulus
180 GPa
Izod impact strength (at 23°C, notched)
150 J
Datasheet
Technology
DMLS
Maximal size for series production
245 x 245 x 270 mm
Maximal size for prototyping
245 x 245 x 270 mm
Heat distortion temperature (at 0.45MPa)
---
Tensile strength at break
900 MPa
Elongation at break
10 %
Flexural modulus
110 GPa
Izod impact strength (at 23°C, notched)
---
Datasheet
Technology
DMLS
Maximal size for series production
440 x 220 x 315 mm
Maximal size for prototyping
500 x 280 x 315 mm
Heat distortion temperature (at 0.45MPa)
---
Tensile strength at break
300 MPa
Elongation at break
2 %
Flexural modulus
70 GPa
Izod impact strength (at 23°C, notched)
---
Datasheet
Technology
DMLS
Maximal size for series production
250 x 250 x 300 mm
Maximal size for prototyping
250 x 250 x 300 mm
Heat distortion temperature (at 0.45MPa)
---
Tensile strength at break
~ 220 MPa
Elongation at break
20 %
Flexural modulus
---
Izod impact strength (at 23°C, notched)
---
Datasheet
Technology
SLA
Maximal size for series production
200 x 125 x 220 mm
Maximal size for prototyping
200 x 125 x 220 mm
Heat distortion temperature (at 0.45MPa)
88°C
Tensile strength at break
75 MPa
Elongation at break
6 %
Flexural modulus
3700 MPa
Izod impact strength (at 23°C, notched)
18.8 J/m
Datasheet
Technology
SLA
Maximal size for series production
140 x 140 x 170 mm
Maximal size for prototyping
140 x 140 x 170 mm
Heat distortion temperature (at 0.45MPa)
77°C
Tensile strength at break
61 MPa
Elongation at break
13 %
Flexural modulus
2200 MPa
Izod impact strength (at 23°C, notched)
18.7 J/m
Datasheet
Technology
MSLA
Maximal size for series production
200 x 125 x 220 mm
Maximal size for prototyping
1100 x 690 x 590 mm
Heat distortion temperature (at 0.45MPa)
72°C
Tensile strength at break
43 MPa
Elongation at break
6 %
Flexural modulus
1500 MPa
Izod impact strength (at 23°C, notched)
2.68 KJ/m2
Datasheet
Technology
MSLA
Maximal size for series production
200 x 125 x 220 mm
Maximal size for prototyping
1100 x 690 x 590 mm
Heat distortion temperature (at 0.45MPa)
62°C
Tensile strength at break
43 MPa
Elongation at break
5 %
Flexural modulus
---
Izod impact strength (at 23°C, notched)
---
Datasheet
Technology
FDM
Maximal size for series production
210 x 210 x 250 mm
Maximal size for prototyping
600 x 600 x 1200 mm
Heat distortion temperature (at 0.45MPa)
55°C
Tensile strength at break
53 MPa
Elongation at break
6 %
Flexural modulus
3800 MPa
Izod impact strength (at 23°C, notched)
16 J/m
Datasheet
Technology
FDM
Maximal size for series production
150 x 150 x 180 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperature (at 0.45MPa)
96°C
Tensile strength at break
45 MPa
Elongation at break
10 %
Flexural modulus
2000 MPa
Izod impact strength (at 23°C, notched)
23 kJ/m²
Datasheet
Technology
FDM
Maximal size for series production
150 x 150 x 180 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperature (at 0.45MPa)
147°C
Tensile strength at break
63 MPa
Elongation at break
2 %
Flexural modulus
3750 MPa
Izod impact strength (at 23°C, notched)
60 kJ/m²
Datasheet
Technology
FDM
Maximal size for series production
250 x 210 x 210 mm
Maximal size for prototyping
500 x 500 x 1200 mm
Heat distortion temperature (at 0.45MPa)
68°C
Tensile strength at break
45 MPa
Elongation at break
25 %
Flexural modulus
1600 MPa
Izod impact strength (at 23°C, notched)
11 kJ/m²
Datasheet
Datasheet
Technology
FDM
Maximal size for series production
150 x 150 x 180 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperatur (at 0.45MPa)
96°C
Tensile strengthe at break
45 MPa
Elongation at break
10 %
Flexural modulus
2000 MPa
Izod impact strength (at 23°C, notched)
23 kJ/m²
Datasheet